Low Smoke Halogen-Free Flame Retardant Polyolefin Insulating Material Irradiated At 125 Temperature
Product Name, Model Type and Usage
Product Model |
Product Name |
Characteristics And Uses |
SH8510-125 |
Low Smoke Halogen-Free Flame Retardant Polyolefin Insulating Material Irradiated at 125 Temperature |
Low temperature resistance - 40 C, burning crust, excellent flame retardant; used for power cables, boats, control and so on. |
Product introduction
SH8510-125 is a low smoke halogen-free flame retardant polyolefin insulating material with good electrical properties. It is mainly used for insulation of power cables, control cables, marine cables, etc. Its long-term service temperature is 125 ℃.
SH8510-125 products meet the requirements of GB/T 19666-2005, IEC60092 and other product standards, and meet the requirements of RoHS and REACH. It is a green environmental flame retardant material.
Product characteristics
·Excellent mechanical properties ·Low smoke emission and corrosiveness
·Excellent electrical performance ·Excellent Extrusion Processing Performance
Processing Guide
The best extrusion effect can be obtained by using 1:1.2 low compression ratio screw. PE/PVC screw extrusion can also be used.
Recommended processing temperature:
position | 1area | 2area | 3area | 4area | 5area | nose | die port |
temperature(℃) | 125 | 135 | 145 | 155 | 160 | 165 | 160-165 |
The melt temperature should be controlled between 165 and 175 degrees C, and the maximum should not exceed 180 degrees C.
If the material is stored in humid environment for a long time, drying treatment is recommended. The drying temperature is 80 C and the drying time is 1-2 hours.
Usually, the measurement of irradiation processing should be controlled at 8-15 Mrad, but ultimately the thermal extension should be taken as the criterion. The optimal control of thermal extension is 50-80%. If oil resistance is required, the thermal extension should be controlled at 20-30%.
Storage and Packaging
It should be stored in a dry and ventilated warehouse.
The products are packed in 25kg paper-plastic composite bags or 500kg container bags.
It can also be packed according to user's requirements.
Technical characteristics
physical property |
unit |
SH8510-125 typical value |
test method |
density |
g/cm3 |
1.45 |
GB/T 1033.1 |
low temperature embrittlement temperature(-40℃)number of failures |
个 |
0 |
GB/T 5470 |
thermal deformation(125℃×4h) |
% |
6 |
GB/T 8815 |
|
|
|
|
mechanical properties |
unit |
SH8510-125 typical value |
test method |
tensile strength |
MPa |
14 |
GB/T 1040 |
elongation at break |
% |
260 |
GB/T 1040 |
thermal aging158℃×7days |
|
|
GB/T 2951.12 |
tensile strength change rate |
% |
+9 |
|
max change of elongation at break |
% |
-6 |
|
thermal extension20N/cm2 200℃×15min |
|
|
GB/T 2951.21 |
load elongation |
% |
48 |
|
permanent deformation |
% |
0 |
|
oil resistance testASTMZ# 100℃×24h |
|
|
GB/T 2951.21 |
tensile strength change rate |
% |
-30 |
|
max change of elongation at break |
% |
+20 |
|
|
|
|
|
electrical performance |
unit |
SH8510-125 typical value |
test method |
20℃ volumetric resistivity |
Ω·m |
2×1013 |
GB/T 1410 |
dielectric strength |
MV/m |
27.8 |
GB/T 1408.1 |
|
|
|
|
combustion performance |
unit |
SH8510-125 typical value |
test method |
oxygen index |
% |
32.5 |
GB/T 2406 |
acid gas |
|
|
GB/T 17650.2 |
conductivity |
us/mm |
0.95 |
|
PH value |
- |
5.6 |
|
maximum smoke density Dm |
|
|
ASTME662 |
smoking method |
|
66 |
|
smoke-free method |
|
200 |
|
toxicity index |
|
1.1 |
NES713 |